Thaum cov cement reacts nrog KFA, lub teeb acetylene roj yuav raug tso tawm, thiab cov roj yuav raug tso tawm sai sai los ntawm cov pob zeb nto kom txo tau tag nrho cov porosity. Cov pores muaj 97% capillary pores thiab 3% coarse pores, thiab cov voids zoo thiab me me. Feem ntau, cov pob zeb feem ntau tsim cov pa roj carbon dioxide, uas yuav tsum tau ntim rau hauv qhov tseem ceeb ua ntej nws tawm ntawm cov pob zeb ua kom muaj qhov sib txawv loj, feem ntau muaj 70% coarse pores thiab 30% zoo pores.
Lub mortar reacts nrog KFA los tsim calcium sulphoaluminate crystals uas yog insoluble thiab tshuaj resistant. Thaum lub sij hawm hydration txheej txheem, nws loj hlob raws phab ntsa ntawm lub capillary los ua ib tug hexagonal dendritic siv lead ua. Thaum cov kua nkag mus, lub hexagonal dendritic siv lead ua nthuav dav, thiab txoj kab uas hla ntawm capillary txo. Lub capillary txoj kab uas hla yog txo, uas yuav ua rau kom lub hydraulic siab thiab cua siab nyob rau hauv lub capillary. Lub zog pem hauv ntej tsim los ntawm cov hlab ntsha tuaj yeem tiv taus roj, kua thiab lwm yam tshuaj electrolytic xws li ntsev, kua qaub, alkaline, kev lag luam pov tseg, suab thaj thiab roj. Kev nkag mus yaig. Nyob rau tib lub sijhawm, noo noo, acid. Alkali tshuaj kua, roj, thiab lwm yam kua tsis nkag mus rau hauv lub zoo capillary pores. Txawm hais tias cov capillary pores me me vim kev nthuav dav thiab kev cog lus ntawm cov siv lead ua, lawv tseem muaj roj permeable.